CF-LIBS; CuNi alloy; Electron density; LA-TOFMS; LIBS; Plasma temperature; Quantitative analysis;LASER-INDUCED BREAKDOWN; QUANTITATIVE ELEMENTAL ANALYSIS; INDUCED PLASMA; SPECTROSCOPY; SPECTROMETRY; EMISSION

LASER induced breakdown spectroscopy (LIBS) has been used for the quantitative analysis of Cu-Ni alloy of known composition (75% Cu, 25% Ni) using the one line calibration free-LIBS (OLCF-LIBS), self-calibration-LIBS (SC-LIBS), calibration free LIBS (CF-LIBS), time of flight-mass spectroscopy (TOF-MS), energy dispersive X-ray spectroscopy (EDX) and X-ray fluorescence spectroscopy (XRF). For the LIBS-based studies, the plasma was generated by focusing the beam of a Q-switched Nd:YAG laser (532 nm, pulse energy about 200 mJ, 5 ns pulse duration) while the sample was placed in air at an atmospheric pressure. Plasma temperature about (9500 +/- 300) K was calculated by the Boltzmann plot method using the neutral lines of Cu and Ni whereas the electron number density was calculated (2.0 +/- 0.5) x 10(16) cm(-3) from the Stark broadening of an isolated Cu line as well as using the relative intensities of the neutral and singly ionized optically thin lines in the Saha-Boltzmann equation. The elemental compositions determined by different LIBS methods and standard techniques are; OLCF-LIBS (69% Cu and 31% Ni), SC-LIBS (72% Cu and 28% Ni), CF-LIBS (74% Cu and 26% Ni), TOF (74% Cu and 26% Ni), EDX (75% Cu and 24.5% Ni), XRF (73% Cu and 24.7% Ni), and LA-TOF (74% Cu and 26% Ni). It is demonstrated that the CF-LIBS method gives compositions comparable with that determined by LA-TOF, EDX, or XRF, which is also in agreement with the certified reported composition.

Laser-induced breakdown spectroscopy; Electron temperature; Number density; Magnetic confinement; Surface structuring;X-RAY-EMISSION; OPTICAL-EMISSION; ELECTRON-DENSITY; CARBON PLASMA; AMBIENT GAS; ABLATION; PLUME; TEMPERATURE; CONFINEMENT; PARAMETERS

The effect of the transverse magnetic field on laser-induced breakdown spectroscopy and surface modifications of germanium (Ge) has been investigated at various fluences. Ge targets were exposed to Nd: YAG laser pulses (1064 nm, 10 ns, 1 Hz) at different fluences ranging from 3 to 25.6 J/cm(2) to generate Ge plasma under argon environment at a pressure of 50 Torr. The magnetic field of strength 0.45 Tesla perpendicular to the direction of plasma expansion was employed by using two permanent magnets. The emission spectra of laser-induced Ge plasma was detected by the laser-induced breakdown spectroscopysystem. The electron temperature and number density of Ge plasma are evaluated by using the Boltzmann plot and stark broadening methods, respectively. The variations in emission intensity, electron temperature (T-e), and number density (n(e)) of Germanium plasma are explored at various fluences, with and without employment of the magnetic field. It is observed that the magnetic field is responsible for significant enhancement of both excitation temperature and number density at all fluences. It is revealed that an excitation temperature increases from T-e,T-max,T-without B = 16,190 to T-e,T-max,T-with B = 20,123 K. Similarly, the two times enhancement in the electron density is observed from n(e,max,without B) = 2 x 10(18) to n(e,max,with B) = 4 x 10(18) cm(-3). The overall enhancement in Ge plasma parameters in the presence of the magnetic field is attributed to the Joule heating effect and adiabatic compression. With increasing fluence both plasma parameters increase and achieve their maxima at a fluence of 12.8 J/cm(2) and then decrease. In order to correlate the plasma parameters with surface modification, scanning electron microscope analysis of irradiated Ge was performed. Droplets and cones are formed for both cases. However, the growth of ridges and distinctness of features is more pronounced in case of the absence of the magnetic field; whereas surface structures become more diffusive in the presence of the magnetic field.

Silicon; Laser-induced breakdown spectroscopy; Emission spectroscopy; Surface morphology; Periodic surface structures;PLASMA PARAMETERS; SURFACE-MORPHOLOGY; SILICON; ZINC; ALLOY; TEMPERATURE; DIAGNOSTICS; SPECTRA; DENSITY; GAS

The effect of nature and pressure of ambient environment on laser-induced breakdown spectroscopy (LIBS) and ablation mechanisms of silicon (Si) have been investigated. A Q-switched Nd-YAG laser with the wavelength of 1064 nm, pulse duration of 10 ns, and pulsed energy of 50 mJ was employed. Si targets were exposed under ambient environments of inert gases of argon, neon, and helium for different pressures ranging from 5 to 760 torr. The influence of nature and pressure of ambient gases on the emission intensity of Si plasma have been explored by using the LIBS spectrometer system. The plasma parameters such as electron temperature and number density were determined by applying Boltzmann plot and Stark broadening method, respectively. Our experimental results suggest that the nature and pressure of ambient environment play a significant role for generation, recombination, and expansion of plasma and consequently affect the excitation temperature as well as electron density of plasma. The surface morphological analysis of laser-irradiated Si was performed by using scanning electron microscope (SEM). Various kinds of structures, for example laser-induced periodic surface structures or ripples, cones, droplets, and craters have been generated and their density and size are found to be strongly dependent upon the ambient environment. A quantitative analysis of particulate size and crater depth measured from SEM images showed a strong correlation between plasma parameters and the growth of micro/nanostructures on the modified Si surface.

Electron number density; Electron temperature; Laser-induced breakdown spectroscopy; Spatial confinement; Spectral emissions;PLASMA; TEMPERATURE; ABLATION; DENSITY

Spatial confinement effects on plasma parameters and surface morphology of laser-ablated Mg are studied by introducing a metallic blocker as well as argon (Ar) gas at different pressures. Nd: YAG laser at various fluences ranging from 7 to 28 J/cm(2) was employed to generate Mg plasma. Confinement effects offered by metallic blocker are investigated by placing the blocker at different distances of 6, 8, and 10 mm from the target surface; whereas spatial confinement offered by environmental gas is explored under four different pressures of 5, 10, 20, and 50 Torr. Laser-induced breakdown spectroscopy analysis revealed that both plasma parameters, that is, excitation temperature and electron number density initially are strongly dependent upon both pressures of environmental gases and distances of blockers. The maximum electron temperature of Mg plasma is achieved at Ar gas pressure of 20 Torr, whereas maximum electron number density is achieved at 50 Torr. It is also observed that spatial confinement offered by metallic blocker is responsible for the significant enhancement of both electron temperature and electron number density of Mg plasma. Maximum values of electron temperature and electron number density without blocker are 8335 K and 2.4 x 10(16) cm(-3), respectively, whereas these values are enhanced to 12,200 K and 4 x 10(16) cm(-3) in the presence of blocker. Physical mechanisms responsible for the enhancement of Mg plasma parameters are plasma compression, confinement and pronounced collisional excitations due to reflection of shock waves. Scanning electron microscope analysis was performed to explore the surface morphology of laser-ablated Mg. It reveals the formation of ripples and channels that become more distinct in the presence of blocker due to plasma confinement. The optimum combination of blocker distance, fluence and Ar pressure can identify the suitable conditions for defining the role of plasma parameters for surface structuring.